How high a temperature can the PP flame retardant in the PP flame-retardant plate withstand?

PP plates can be processed by extrusion during production. In the extrusion molding process, after the materials in granular solid state enter the extruder, they need to complete the processes of conveying, compacting, melting, homogenizing until the high-temperature molten parison is extruded from the machine head, and the temperature change during this process is very complex. The flame retardant mixed with the PP material should also be able to withstand high temperatures. 

Generally, the processing temperature of PP plates is around 170-190 degrees Celsius. For some processes with special requirements, the processing temperature is even higher. Since the temperature inside the barrel during heating, especially the temperature of the shear block, is significantly higher than the processing temperature. Generally, the decomposition temperature or thermal weight loss temperature of the flame retardant must be at least 20 degrees Celsius higher than the processing temperature. This requires that the flame retardant in the PP flame-retardant plate should be able to withstand a high temperature of at least above 230°C.